Bond Performance of Sand Coated UHM CFRP Tendons in High Performance Concrete
Lämmlein, Tobias D.
Terrasi, Giovanni P.
- Journal Article
Rechte / LizenzCreative Commons Attribution 4.0 International
The bond behaviour of novel, sand-coated ultra-high modulus (UHM) carbon fibre reinforced polymers (CFRP) tendons to high performance concrete (HPC) was studied by a combined numerical and experimental approach. A series of pull-out tests revealed that the failure type can vary between sudden and continuous pull-out depending on the chosen sand coating grain size. Measuring the same shear stress vs. tendon draw-in ( - ) curves in the same test set-up, for sand coated CFRP tendons with a longitudinal stiffness of 137 and 509 GPa, respectively, indicated that the absolute bond strength in both cases was not influenced by the tendon’s stiffness. However, the - curves significantly differed in terms of the draw-in rate, showing higher draw-in rate for the UHM CFRP tendon. With the aid of X-ray computed tomography (CT), scanning electron microscopy (SEM) and visual analysis methods, the bond failure interface was located between the CFRP tendon and the surrounding sand-epoxy layer. For further investigation, a simplified finite element analysis (FEA) of the tendon pull-out was performed using a cohesive surface interaction model and the software Abaqus 6.14. A parametric study, varying the tendon-related material properties, revealed the tendon’s longitudinal stiffness to be the only contributor to the difference in the - curves found in the experiments, thus to the shear stress transfer behaviour between the CFRP tendon and the concrete. In conclusion, the excellent bond of the sand-coated UHM CFRP tendons to HPC as well as the deeper insight in the bond failure mechanism encourages the application of UHM CFRP tendons for prestressing applications. Mehr anzeigen
Zeitschrift / SeriePolymers
Seiten / Artikelnummer
ThemaCFRP; UHM carbon fibre; UTS carbon fibre; prestressing tendon; sand coated; bond; HPC; Pull-out test; Finite element modelling (FEM); X-ray tomography