Microstructure of selective laser melted nickel-titanium
METADATA ONLY
Loading...
Author / Creator
Date
2014-08
Publication Type
Journal Article
ETH Bibliography
yes
Citations
Altmetric
METADATA ONLY
Data
Rights / License
Abstract
In selective laser melting, the layer-wise local melting of metallic powder by means of a scanning focused laser beam leads to anisotropic microstructures, which reflect the pathway of the laser beam. We studied the impact of laser power, scanning speed, and laser path onto the microstructure of NiTi cylinders. Here, we varied the laser power from 56 to 100 W and the scanning speed from about 100 to 300 mm/s. In increasing the laser power, the grain width and length increased from (33 ± 7) to (90 ± 15) μm and from (60 ± 20) to (600 ± 200) μm, respectively. Also, the grain size distribution changed from uni- to bimodal. Ostwald-ripening of the crystallites explains the distinct bimodal size distributions. Decreasing the scanning speed did not alter the microstructure but led to increased phase transformation temperatures of up to 40 K. This was experimentally determined using differential scanning calorimetry and explained as a result of preferential nickel evaporation during the fabrication process. During selective laser melting of the NiTi shape memory alloy, the control of scanning speed allows restricted changes of the transformation temperatures, whereas controlling the laser power and scanning path enables us to tailor the microstructure, i.e. the crystallite shapes and arrangement, the extent of the preferred crystallographic orientation and the grain size distribution. © 2014 Elsevier Inc.
Permanent link
Publication status
published
External links
Editor
Book title
Journal / series
Volume
94
Pages / Article No.
189 - 202
Publisher
Elsevier
Event
Edition / version
Methods
Geographic location
Date collected
Date created
Subject
Shape memory alloy; NiTi; Selective laser melting; Differential scanning calorimetry; Electron backscatter diffraction; Anisotropic grain
Organisational unit
Notes
Received 9 November 2013, Revised 19 May 2014, Accepted 24 May 2014, Available online 27 May 2014.